Low Carbon Wire Rod
Table of content
The product
The Pittini Group is a reference in the field of production and supply of high quality low carbon content wire rod and provides excellent logistic and packaging service to customers.
Wire rod for drawn wires is manufactured so as to obtain the best drawing with good surface finish. Therefore it is suitable for chemical pickling and mechanical descaling. It is produced in qualities that allow to reach diameter reductions lower than one millimeter or in grades having silicon contents that ensure the best hot zinc plating can be obtained. Boron wire rods are very ductile and can achieve larger cross-section reductions while still being highly workable.
Wire rod for reinforced concrete structures is designed so that the resulting products, after processing – cold rolled wires, electro-welded meshes and lattice girders – comply with the specifications laid down in the regulations in force in Italy and abroad.
Also wire rod Fe36 is worth mentioning, as it meets the features required by steel S235JR according to norm EN 10025-2, as per the European Regulation 305/2011 no.Fe36-CPR-2013-07.
Wire rod for welding wires has low impurity contents to ensure proper behaviours when further processed, with fast diameter reductions and related mechanical stress relieving.
The wire rod produced in Osoppo obtained the EPD Certification – Environmental Product Declaration – by the certifying partner ICMQ, the Institute for certification and quality branding for products and services for construction.
Low Carbon Wire Rod for Concrete Reinforcement
| Type | Classification | Technical sheet | Applications |
Fe41 Sta (SAE 1008 Mesh Quality) |
ASTM A 510M SAE 1008 |
SPF157i | Drawing and cold rolling for production of concrete reinforcing |
GVD/A |
EN ISO 16120 |
SPV006i | |
SAE 1010 (Mesh Quality) |
ASTM A 510M SAE 1010 |
SPF709i |
Low Carbon Content For Drawing
| Type | Classification | Technical sheet | Applications |
Fe 34+B |
ASTM A 510M SAE 1005 e SAE 1006,
|
SPF154i | For deep drawing and cold rolling |
G3V5/B |
ASTM A 510M SAE 1005 e SAE 1006,
|
||
G3v6/B |
UNI EN ISO 16120-2 C4D |
SPV003i | |
Fe 36 (S235JR) |
ASTM A 510M SAE 1006,
|
SPF166i DoP Fe36i |
For cold drawing and rolling, suitable for steel structures according to EN 10025 |
Fe37
|
ISO16120-2 C4D,
|
SPF141i DoP Fe37i |
For cold drawing and rolling, Suitable for hot dip galvanizing, Suitable for steel structures according to EN 10025 |
Fe37 + B |
EN ISO 16120-2 C4D |
SPF140i | For drawing and cold rolling. Suitable for hot dip galvanizingFor drawing and cold rolling |
G3V8/B |
EN ISO 16120-2 C4D |
SPV002i | |
SAE 1006(*) |
ASTM A 510M SAE 1006,
|
SPV009i | For drawing and cold rolling |
SAE 1008(*) |
ASTM A 510M SAE 1008,
|
SPV004i | For drawing and cold rolling |
SAE 1010(*) |
ASTM A 510M SAE 1010,
|
SPV005i | For drawing and cold rolling |
G3V20 |
EN ISO 16120-4 C20D2 |
SPV012i | For drawing |
(*) = on request